发表刊物：JOURNAL OF ALLOYS AND COMPOUNDS
关键字：Li(Ni0.6Co0.2Mn0.2)O-2 cathode materials Testing temperature Electrochemical performance Equivalent circuit model Ti3C2(OH)(2) modification
摘要：The effects of testing temperature on the electrochemical properties of Li(Ni0.6Mn0.2Co0.2)O-2 are investigated in detail. When the testing temperature is 40 degrees C, the Li(Ni0.6Mn0.2Co0.2)O-2 cathode material possesses the highest initial discharge capacity of 162.4 mAh.g(-1) at 0.5C rate, but their cycling stability decreases markedly. When the test temperature rises up to 60 degrees C, the side reaction between electrolyte and cathode material becomes serious, and the Li(Ni0.6Mn0.2Co0.2)O(2 )cannot work. When the testing temperature decreases, the electrochemical impedances like R-ct values increase, and then the discharge capacity at 0 degrees C, -10 degrees C and -20 degrees C is only 80%, 53% and 23% of that at 25 degrees C. Based on the electrochemical impedance spectra at different temperatures, four kinds of equivalent circuit models are classified. The cycle and rate performance of Li(Ni0.6Mn0.2Co0.2)O-2 cathode material could be improved obviously through Ti3C2(OH)(2) modification in an extreme environment, and especially in sub-zero environment. (C) 2019 Elsevier B.V. All rights reserved.
ISSN号：0925-8388
是否译文：否
发表时间：2019-10-05
合写作者：Xu, Lipeng,周飞,孔继周,Zhou, Haobin,张强
通讯作者：周飞,孔继周,周菲菲