发表刊物:JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE
关键字:carbon content CrTiAlCN coatings friction coefficient wear
摘要:Multi-component CrTiAlCN coatings with different carbon contents were deposited on AISI M2 high-speed steels using unbalanced magnetron sputtering via adjusting the C2H2 flow rates, and their microstructures and mechanical properties were characterized by using SEM, EDS, XRD, Vickers hardness tester and scratch tester, respectively. The tribological properties of CrTiAlCN coatings sliding against SUS440C high carbon martensitic balls were performed using ball-on-disk tribo-tester. The results showed that CrTiAlCN coatings were mainly comprised of (111) and (200) crystal orientation. The maximum hardness of coatings was 29.4 +/- 1.5 GPa as the carbon content was 22.5 at.%. With an increase in the carbon content of coatings, the friction coefficients and wear rates of CrTiAlCN/SUS440C tribo-pairs were significantly reduced, and the wear mechanism of coatings changed from adhesive wear to abrasive wear.
ISSN号:1059-9495
是否译文:否
发表时间:2019-03-01
合写作者:Zhang, Maoda,周飞,Fang, Haotian,Wu, Zhiwei,王谦之,孔继周
通讯作者:周飞,周菲菲