Influence of Cr Content on Corrosion Behaviour of Tube Pile Steel in Half-Immersion Environment

点击次数:

所属单位:材料科学与技术学院

发表刊物:TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS

关键字:Tube pile steel Cr Corrosion behaviour Half-immersion environment

摘要:Corrosion behaviour of tube pile steel produced by thermo-mechanical controlled processing (TMCP) technology with Cr addition ranging from 0.5 to 2.0 wt% in half-immersion environment were investigated. Results indicated that the most serious corrosion occurred in the liquid-air interface zone and the corrosion type transformed from pitting corrosion to uniform corrosion gradually with the increasing addition of Cr. Increasing addition of Cr reduced the pit depth of steel, but did not decrease the overall corrosion rate of steel during the 5 months' half-immersion corrosion due to the microstructure transformation with the increase of Cr content.

ISSN号:0972-2815

是否译文:

发表时间:2018-01-01

第一作者:刘希琴

通讯作者:刘希琴,刘希琴,刘希琴,刘希琴,刘希琴,刘希琴,刘希琴,刘希琴,刘希琴,刘希琴,刘希琴,刘子利,刘子利,刘子利,刘子利,刘子利,刘子利,刘子利,刘子利

其他作者:刘子利,刘子利,刘子利,刘子利,刘子利,刘子利,刘子利,刘子利,刘子利,刘子利,刘子利,刘子利,刘子利,刘子利,刘子利,刘子利,刘子利,刘子利,刘子利,刘子利,刘子利,刘子利,刘子利,刘子利,刘子利,刘子利,刘子利,刘子利,刘子利,刘子利,刘子利,刘子利,刘子利,刘子利,胡金东,侯志国,田青超,王怀忠