陈照峰
开通时间:..
最后更新时间:..
点击次数:
所属单位:材料科学与技术学院
发表刊物:Inorg. Chem. Front.
摘要:A double network nested foam composite with tunable electromagnetic wave absorption performance was fabricated via a carbonization, impregnation, and chemical vapor infiltration method. The research results indicated that the three-dimensional interconnected carbon foam was successfully enhanced by the SiC nanowire network. As expected, the electromagnetic absorption performance of the as-prepared SiC nanowire reinforced carbon foam (SiCnw/CF) was greatly improved by the introduction of the SiC nanowires. The SiCnw/CF composite prepared with a lower concentration of Ni catalyst possessed an excellent microwave absorption property with the lowest reflection loss value of -36.31 dB with a matched thickness of 2.60 mm accompanied by the widest effective bandwidth of 4.52 dB. An increase in catalyst concentration degraded the electromagnetic absorption ability to a certain extent. A potential microwave absorption schematic diagram was finally proposed, and it stated that the SiC nanowire network played an essential role in the improvement of the electromagnetic absorption properties. © 2019 the Partner Organisations.
是否译文:否
发表时间:2019-06-01
合写作者:Ye, Xinli,Zhang, Junxiong,Wu, Cao,曹瑞武,Zhou, Qianbo,Ai, Sufen,Liu, Hezhou,Cui, Sheng
通讯作者:Ye, Xinli,陈照峰