发表刊物：JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE

关键字：Al-Cu-Mg alloy morphological evolution S-phase tensile creep

摘要：The morphological evolution behavior of S-phase in 2024 aluminum alloy under uniaxial tensile creep test at 448 and 463K under 175, 200 and 225MPa was studied in detail by HRTEM. Results showed that the S-phase was arranged in the zigzag manner, similar to a zebra pattern, under tensile stress at 448-463K. And it maintained cubic structure, remarkably grew along the tension direction under uniaxial tensile stress, but grew minimally perpendicular to the stress direction. Compared with applied stress, the temperature had a greater effect on the growth of S-phase. The length of S-phase reached 100 +/- 20nm after testing for 24h at 448K under 200MPa and 200 +/- 50nm after testing for 18h at 463K under 175MPa. The S-phase not only grew significantly in length but also coarsened at 463K, the lamellar structure becoming fuzzy, which caused the alloy to enter the tertiary creep stage, unsuitable for creep-aging forming.

ISSN号：1059-9495

是否译文：否

发表时间：2019-06-01

合写作者：Yang, Kai,张平则,Li, Fengkun,Liang, Hongxuan,姚正军

通讯作者：魏东博