摘要：Cobalt doped zinc oxide nanopowders were prepared via solid-state reaction. The influences of calcining temperatures on crystal structure, morphology, emissivity and color change of the Zn1-xCoxO nanopowders were studies detailedly. The results indicate that the substitute for Zn2+ by Co2+ in hexagonal wurtzite ZnO usefully sintering temperatures are 900–1200 °C. Moreover, the crystallinity, the oxygen vacancy content and the amount of Co2+ substituted Zn2+ in the Zn1-xCoxO nanopowders are increasing with the heating temperature improving. All the samples show reversible thermochromism, which can reversible color change from green to yellow by rising test temperature from 25 to 800 °C. Meanwhile, the largest emissivity change is 0.321 as the test temperature changes between 25 and 800 °C in the sample heated at 1100 °C. The Zn1-xCoxO has great potential applications for smart adaptive camouflage in visible-infrared region. © 2018 Elsevier B.V.

ISSN号：0925-3467

是否译文：否

发表时间：2018-12-01

合写作者：徐诚,徐国跃,Xiang, Shanshan,Zhu, Yongmei

通讯作者：王长波