所属单位:理学院
发表刊物:JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS
关键字:NdFe2 laves compounds Melt-spinning Magnetostrictive properties
摘要:A series of Tb0.2Nd0.8(Fe1-xCox)(1.9) (0.0 <= x 6 <= 0. 4) Laves ribbons were prepared by arc-melting and subsequent melt-spinning technique. The effects of Co substitution for Fe on the structural and magnetostrictive properties of Tb0.2Nd0.8Fe1.9 ribbons were investigated. Tb0.2Nd0.8Fe1.9 ribbons consist of (Tb, Nd) Fe-2 Laves phase and a minor of rare earth but free of (Tb, Nd) Fe-3 phase. Almost single Laves ribbons can be obtained when x >= 0.1, which indicates that the Co substitution for Fe is beneficial for the formation of Laves ribbons. The lattice parameter of the Laves ribbons decreases with increasing x. The Curie temperature of the Laves phase and saturation magnetization of the ribbons both get maximum at x = 0.2. Meanwhile, the magnetostriction Tb0.2Nd0.8Fe1.9 ribbons can be improved by a proper amount of substitution of Co for Fe. (C) 2017 Elsevier B.V. All rights reserved.
ISSN号:0304-8853
是否译文:否
发表时间:2017-07-01
合写作者:Wang, L.,Zheng, W. G.,Chen, Z. Y.,施大宁
通讯作者:时阳光