发表刊物:JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS
关键字:Cubic Laves compound Magnetocaloric effect Transition order
摘要:The magnetocaloric effect (MCE) and transition order in Nd(Co0.8Fe0.2)(2) Laves phase compound were studied by dc magnetization measurement. In order to make the inexpensive NdCo2 Laves phase compound for room-temperature magnetic refrigeration possible, the Curie temperature of the NdCo2 (similar to 100 K) was tuned to 263 K with 20 at.% of Fe substituting for Co. An entropy change of 1.66 J/kg K was obtained in Nd(Co0.8Fe0.2)(2) at 265 K under an external magnetic field change of 30 kOe. Meanwhile, a wide operating temperature range of 102 K for MCE and a large refrigerant capacity of 121.6 J/kg at an external field change of 30 kOe were observed. Specially, at an external field change of 20 kOe, the operating temperature of Nd(Co0.8Fe0.2)(2) (81 K) is even twice wider than that of Gd (39 K). To confirm the transition order of the compound, Banerjee criterion as well as the universal scaling of the magnetocaloric effects were employed. These two criteria agree well with each other, indicating a second-order transition in Nd(Co0.8Fe0.2)(2). (C) 2018 Elsevier B.V. All rights reserved.
ISSN号:0304-8853
是否译文:否
发表时间:2018-08-15
合写作者:Zheng, W. G.,Cui,Y,Chen, F. H.,施大宁
通讯作者:时阳光