点击次数：
所属单位：材料科学与技术学院
发表刊物：JOURNAL OF ADHESION SCIENCE AND TECHNOLOGY
关键字：Friction stir welding aluminum alloy disk microstructure mechanical properties
摘要：In this study, a modified stir tool with a disk at the top of the probe was used for friction stir welding (FSW) of 6061-T6 aluminum alloy. The effect of the disk at the top of the probe on the thermal history, microstructure and mechanical properties of the resulting FSW joints was investigated. The results showed that the disk could increase the peak temperature, prolong the thermal cycle and improve the material flow at the welded bottom. As a result, root defects were eliminated and the microstructure of weld bottom was homogenized and refined due to more sufficient dynamic recrystallization. The tensile strength of FSW joint produced using the probe with a top disk was about 243 MPa, reaching 77.9% of the BM, while that of FSW joint produced by the probe without a top disk was only 204 MPa, as much as 65.4% of the BM acquired. The FSW joint produced by the modified tool exhibited ductile fracture with the cracks initiated and propagated from the softening zone, while a mixed-mode of ductile and brittle fractures occurred in the FSW joint produced by conventional tool, which originated from root defects at the bottom of the weld.
ISSN号：0169-4243
是否译文：否
发表时间：2019-11-17
合写作者：Huang, Guoqiang,Cheng, Dongxu,Wang, Haoming,Zhou, Qihui
通讯作者：沈以赴