所属单位：机电学院
发表刊物：INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE
关键字：Sintered NdFeB Interlaced jet electrodeposition Periodic gradient multilayer coating Adhesion strength Corrosion resistance
摘要：Jet electrodeposition is an effective method to prepare protective coatings on NdFeB. To improve the performance of interlaced multilayer coatings, layers that changed periodically and gradiently were prepared by changing the current density for even layers. The surface morphology and microstructure of the coatings were characterized by scanning electron microscopy and X-ray diffraction. The adhesion strength, microhardness, and corrosion resistance of the coatings were measured using an automatic scratch tester, a microhardness tester, and an electrochemical workstation. The results indicated that compared with other coatings, the periodic gradient multilayer coatings obtained a flatter surface and a higher corrosion resistance. In addition, the adhesion strength was increased from 9.2N to 21.7N, and the microhardness was increased from 484HV to 539HV.
ISSN号：1452-3981
是否译文：否
发表时间：2018-08-01
合写作者：范明智,邱明波,汪展文,田宗军
第一作者：沈理达
通讯作者：沈理达