Isothermal oxidation behavior of NiCoCrAlY/ZrO2 composite coating on gamma-TiAl alloy

Affiliation of Author(s):材料科学与技术学院

Journal:MATERIALS RESEARCH EXPRESS

Key Words:gamma-TiAl alloy NiCoCrAlY/ZrO2 composite coating interdiffusion high temperature oxidation magnetron sputtering

Abstract:In this study, a composite NiCoCrAlY/ZrO2 coating was applied to enhance the property of oxidation resistance on the surface of gamma-TiAl alloys ultilizing radio frequency magnetron sputtering. The phase formation, microstrure and chemical composition of the coatings were investigated by x-ray diffraction (XRD) and scanning electron microscopy(SEM). The interlayer binding force was analyzed using scratch test. Further, static oxidation test was carried out at 950 degrees C and the oxidation behavior of the coating was investigated. The results indicated the NiCoCrAlY/ZrO2 coating showed high adhesion strength (critical load > 57.5 N) and the oxidation of the coating obeyed a parabolic law. Above all, the oxidation resistance of the substrate was remarkably enhanced after introducing the NiCoCrAlY/ZrO2 coating. The oxidation resistance enhancement could be attributed to the formation of a protective Al2O3 scale. Besides, the ceramic layer ZrO2 blocked the infiltration of O atoms during high-temperature oxidation.

ISSN No.:2053-1591

Translation or Not:no

Date of Publication:2018-06-01

Co-author:Ding, Zheng,Miao, Qiang,Yang, Zhengang,Lin, Hao

Correspondence Author:Ding, Zheng,Miao, Qiang,lwp

Date of Publication:2018-06-01