所属单位：材料科学与技术学院
发表刊物：ACS SUSTAINABLE CHEMISTRY & ENGINEERING
关键字：Superhydrophobic surface Wettability Electroplating Corrosion prevention
摘要：The corrosion of metal materials is detrimental to petroleum pipelines, marine ships, heat exchangers, etc. To date, existing technologies have focused on improving corrosion resistances, such as anodization and painting. Superhydrophobic surfaces, which can retain air gaps between the corrosive liquids and solid structures, have shown effective corrosion prevention, but the inherent material property is not corrosion resistant. Herein, we reported a novel superhydrophobic surface with excellent corrosion resistance by using an electroplating method. The superhydrophobic surface consists of Zn-Ni and Zn-Co alloys, which are inherently corrosion resistant. We compared such a newly developed surface with superhydrophobic NiO/ZnO and ZnO coatings, respectively. The water contact angle of the novel superhydrophobic coating was larger than 150 degrees after immersion into a NaCl solution for 48 h, while the other two coatings lost the superhydrophobicity. Furthermore, electrochemical measurement results demonstrated that our newly developed superhydrophobic coating exhibited the highest corrosion potential (-0.777 V) and lowest corrosion density (1.905 X 10(-6) A cm(-2)). We envision that the inherently anticorrosion superhydrophobic coating can effectively prevent the corrosion of industrial metals.
ISSN号：2168-0485
是否译文：否
发表时间：2018-04-01
合写作者：Xiang, Tengfei,Han, Yang,Guo, Zongqi,Wang, Rong,Zheng, Shunli,Li, Sheng,Dai, Xianming
通讯作者：李澄,Dai, Xianming,李澄
发表时间：2018-04-01