Extension of Puck's inter fibre fracture (IFF) criteria for UD composites
点击次数：
所属单位：
航空学院
发表刊物：
COMPOSITES SCIENCE AND TECHNOLOGY
关键字：
Failure criterion Strength Transverse cracking Puck's IFF criteria
摘要：
Puck's action plane failure criteria have already proven their capability in the first and second world-wide failure exercises (WWFE-I and WWFE-II). However, Puck and his co-workers have only recommended inclination parameters for GFRP/Epoxy and CFRP/Epoxy. These UD composites generally have high transverse compressive-to-tensile strength ratios Y-C/Y-T, and are regarded by them as intrinsically brittle materials. Therefore, Pucks inter fibre fracture (IFF) criteria might not be directly applied to other types of UD composites with low Y-C/Y-T ratios. In particular, Puck's original IFF criteria will result in unrealistic predictions if Y-C/Y-T is extremely low. In the present study, Pucks original IFF criteria are extended to all types of UD composite materials to solve the problem. Composites are divided into three categories, namely semi-brittle materials, brittle materials, and intrinsically brittle materials. Depending on the material category, three different algorithms are proposed for determination of the two parameters in Puck's IFF criteria, namely the resistance of the action plane against transverse tensile stressing, R-perpendicular to(At), as well as the inclination parameter of contour lines of the fracture body, p(perpendicular to perpendicular to). The present criteria are theoretically evaluated for composites with low Y-C/Y-T ratios, while the predictions of the present criteria are compared with the test results of composites with high Y-C/Y-T ratios such as thermoset GFRP and CFRP. Theoretical and experimental assessment demonstrates the reasonableness of the extension of Pucks IFF criteria.
ISSN号：
0266-3538
是否译文：
否
发表时间：
2018-07-07
合写作者：
Gu, Jiefei
通讯作者：
陈普会
发表时间：
2018-07-07
学位：工学博士学位
职称：教授
所在单位：航空学院