Key Words:NiCoCrAlY/ZrO2 duplex coating high temperature gamma-TiAl alloy friction coefficient wear mechanism
Abstract:A dense NiCoCrAlY/ZrO2 duplex coating was deposited onto the gamma-TiAl alloy by magnetron sputtering technology for the purpose of improving its friction and wear properties at high temperature. Some tests of the ball-on-disk type that were against Si3N4 counterpart, were performed at room temperature and 500 degrees C. The average friction coefficients as well as the wear rates of NiCoCrAlY/ZrO2 duplex coatings were greatly less than those of substrates at both temperatures. Besides, the H/E and H-3/E-2 value of the NiCoCrAlY/ZrO2 coatings were much higher than that of the substrate. The excellent wear-resisting property of NiCoCrAlY/ZrO2 duplex coating was caused by the synergistic effect of its high hardness and outstanding plastic-deformation resistance.
ISSN No.:2053-1591
Translation or Not:no
Date of Publication:2019-08-01
Co-author:丁铮,lwp,杨振刚,安浩,易锦伟,林浩
Correspondence Author:zq