摘要：A series of (Tb0.2Pr0.8)xDy1-xFe1.93 (0.3 ≤ x ≤ 1.0) Laves compounds was prepared using a high-pressure annealing method. These compounds exhibit a multiphase behaviour when prepared by traditional annealing methods whereas they present a single Laves phase when synthesised by high-pressure annealing. The Curie temperature of the Laves compounds decreases with the increasing atomic ratio x. However, the saturation magnetisation does not increase monotonically but goes through a minimum with increasing x. A structural transition from tetragonal to rhombohedral was observed as x increased from 0.6 to 0.7. The magnetostriction decreased slightly with increasing x in the tetragonal phase region and then increased rapidly during the transition from tetragonal to rhombohedral phase at x = 0.7. Furthermore, large low-field magnetostriction and low anisotropy were achieved simultaneously in the (Tb0.2Pr0.8)0.7Dy0.3Fe1.93 compound. © 2018 Elsevier Ltd

ISSN号：0025-5408

是否译文：否

发表时间：2019-04-01

合写作者：Liu, Y.D.,刘彦东,阚彩侠,时阳光,施大宁

通讯作者：张广斌