Title of Paper:Structure and magnetostriction in (Tb0.2Pr0.8)xDy1 -xFe1.93 Laves compounds synthesised by high-pressure annealing

Hits:

Affiliation of Author(s):理学院

Journal:Mater Res Bull

Abstract:A series of (Tb0.2Pr0.8)xDy1-xFe1.93 (0.3 ≤ x ≤ 1.0) Laves compounds was prepared using a high-pressure annealing method. These compounds exhibit a multiphase behaviour when prepared by traditional annealing methods whereas they present a single Laves phase when synthesised by high-pressure annealing. The Curie temperature of the Laves compounds decreases with the increasing atomic ratio x. However, the saturation magnetisation does not increase monotonically but goes through a minimum with increasing x. A structural transition from tetragonal to rhombohedral was observed as x increased from 0.6 to 0.7. The magnetostriction decreased slightly with increasing x in the tetragonal phase region and then increased rapidly during the transition from tetragonal to rhombohedral phase at x = 0.7. Furthermore, large low-field magnetostriction and low anisotropy were achieved simultaneously in the (Tb0.2Pr0.8)0.7Dy0.3Fe1.93 compound. © 2018 Elsevier Ltd

ISSN No.:0025-5408

Translation or Not:no

Date of Publication:2019-04-01

Co-author:Liu, Y.D.,lyd,Kan Caixia,Shi Yangguang,Shi Daning

Correspondence Author:zgb