Study on the micro-crack evolution of concrete subjected to stress corrosion and magnesium sulfate

Affiliation of Author(s):航空学院

Journal:CONSTRUCTION AND BUILDING MATERIALS

Key Words:Concrete Durability Stress corrosion Sulfate attack Crack density

Abstract:The deterioration processes of two types of concrete under chemical corrosion (MgSO4), tensile loading coupled with chemical corrosion or flexural loading coupled with chemical corrosion were investigated in this study. Tensile stress and flexural stress loading devices that were designed by the authors were used. A relative dynamic elastic modulus test using the ultrasonic method was utilized, and through the derivation of empirical equations, a crack density model was obtained to describe the concrete damage process. Furthermore, scanning electron microscopy (SEM) was used to investigate the microstructure changes inside the concrete. The results indicated that the flexural and tensile loads significantly affected the deterioration of concrete when combined with magnesium sulfate. Exposure to magnesium sulfate coupled with tensile loading is a harsh environment for concrete. The rate of concrete deterioration under different stress conditions at the same loading level is ranked as follows: tensile stress coupled with chemical corrosion > flexural stress coupled with chemical corrosion > chemical corrosion. (C) 2017 Elsevier Ltd. All rights reserved.

ISSN No.:0950-0618

Translation or Not:no

Date of Publication:2017-06-15

Co-author:Tan, Yongshan,mhy,Zhang, Yunqing,Wu, Chengyou

Correspondence Author:yhf

Date of Publication:2017-06-15