发表刊物:INTERNATIONAL JOURNAL OF AERONAUTICAL AND SPACE SCIENCES
关键字:T-joint Composite structure Low velocity impact Delamination
摘要:The purpose of this paper is to investigate the influence of fixed L-ribs on the damage behavior of integrated composite T-joints subject to low velocity impact. Experimental test is performed on a vertical drop-weight testing device with two different impact energies. Detailed inspection by visual and ultrasonic C-scan reveals that different impact energies result in different damage types and shapes. Experimental results show that without fixed L-ribs the impact caused an elliptical damage around the impact point at the impact energy of 4.45J/mm and a trumpet delamination at the impact energy of 8.90J/mm. In comparison, the impact only caused serious damage around the impact point without delamination at the impact energy of 8.90J/mm with fixed L-ribs. This experimental study has demonstrated that fixing the L-ribs is an effective way to prevent the delamination of the integrated composite T-joint subject to low velocity impact.
ISSN号:2093-274X
是否译文:否
发表时间:2019-06-01
合写作者:Zhu, Rujian,毛春见
通讯作者:许希武