点击次数：

所属单位：材料科学与技术学院

发表刊物：APPLIED SURFACE SCIENCE

关键字：Molybdenum oxide Microbiologically influenced corrosion SRB Mechanical properties Antibacterial property

摘要：In this investigation, a MoO3-SiO2 nanocomposite coating was developed on a 316L stainless steel (SS) substrate by double-cathode glow discharge deposition. Chemical valence states, phase composition and microstructure features of the nanocomposite coating were studied using X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). It was found that the nanocomposite coating was composed of a mixture of crystalline MoO3 and amorphous phases, in which amorphous SiO2 phase was embedded between the hexagonalstructured MoO3 grains with an average grain size of similar to 8.4 nm. Nanoindentation and scratch tests, together with SEM and TEM observation of locally deformed regions, indicated that the nanocomposite coating exhibited high load-bearing capacity due to a combination of high hardness and good adhesion. Contact angle measurements suggested that the nanocomposite coating was more hydrophobic than uncoated 316L SS. The anti-bacterial activity of the MoO3-SiO2 nanocomposite coating against two bacterial strains (E. coli and S. aureus) was determined by the spread plate method. This showed that both bacterial strains exposed to the coating suffered a significant loss of viability. The influences of sulfatereducing bacteria (SRB) on the electrochemical behavior of the MoO3-SiO2 nanocomposite coating in modified Postgate's C seawater (PCS) medium were investigated through potentiodynamic polarization and electrochemical impedance spectroscopy (EIS). The electrochemical tests revealed that the coating had a greater resistance to microbiologically influenced corrosion induced by SRB than uncoated 316L SS. This was corroborated by electrochemical testing (potentiodynamic polarization and EIS), in conjunction with SEM observations of the corroded surfaces. (C) 2018 Elsevier B.V. All rights reserved.

ISSN号：0169-4332

是否译文：否

发表时间：2018-07-31

合写作者：孙腾腾,Jiang, Shuyun,Munroe, Paul,Xie, Zong-Han

通讯作者：徐江