发表刊物：Opt Mater

摘要：In this paper, Co doped TiO2 powders were prepared through solid-state reaction. The effects of sintering temperature on microstructures, morphologies, variable color and emissivity properties of the Co doped TiO2 powders were investigated in detail. The results show that Co2+ ions substitute for Ti4+ ions effectively in rutile TiO2 after heat-treating at 900 °C–1200 °C. Increasing sintering temperature from 900 °C to 1200 °C improves crystalline quality, substitution amount of Co2+ for Ti4+ and oxygen concentration of the Co doped TiO2 powders. All the Co doped TiO2 powders show reversible thermochromism, which are green at room temperature and yellow at testing temperature of ∼800 °C. Simultaneously, the maximum variation of infrared emissivity reaches to 0.332 with testing temperature changing from room temperature to 800 °C in the powders sintered at 1100 °C. The Co doped TiO2 powders are competitive materials for smart stealth compatible visible light and infrared wavebands. © 2018

ISSN号：0925-3467

是否译文：否

发表时间：2018-11-01

合写作者：Xiang, Shanshan,F70206595,Bu, Honghan,Zhang, Yanting

通讯作者：Xiang, Shanshan,徐国跃