Synthesis, characterization and dielectric properties of xBaTi(4)O(9)-(1-x)BaSm2Ti4O12

点击次数: 所属单位:电子信息工程学院 发表刊物:JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS 关键字:SOLID-SOLUTIONS CRYSTAL-STRUCTURE MICROWAVE CERAMICS SYSTEM SM ND TEMPERATURE LN 摘要:Temperature stable microwave dielectric materials xBaTi(4)O(9)-(1 - x)BaSm2Ti4O12 were produced through a conventional solid-state reaction procedure in the work. The structural and microwave dielectric properties of the ceramics were determined with the purpose of finding a microwave ceramics with high dielectric constant (epsilon(r)), high quality factor (Q x f) and zero temperature coefficient of resonant frequency (tau(f)). Experimental results showed that BaTi4O9 additions affected grain growth and densification, the grain size distribution, and tuned the dielectric properties of the produced ceramics. The amount of BaTi4O9 strongly influenced the densification and the microstructure (i.e. grain shape and size) of the produced ceramics. Analysis of the experimental results suggests that the microstructural features can be correlated to the dielectric properties of these ceramics. Accordingly, the dielectric constant (epsilon(r)) and the temperature coefficient of resonant frequency (tau(f)) of the produced BaSm2Ti4O12 ceramics can be tuned with the amount of BaTi4O9 additions and the sintering process parameters. The best dielectric properties were achieved for BaSm2Ti4O12 ceramics with 15% BaTi4O9 (epsilon(r) = 66, Qxf = 15,730 GHz and tau(f) ae 0 ppm/A degrees C). Experimental results suggest that BaTi4O9 doping improves the dielectric properties of the sintered BaSm2Ti4O12 perovskite ceramics, which are further enhanced by doping with BaTi4O9 in small amounts. However, further increase of BaTi4O9 content jeopardizes them. ISSN号:0957-4522 是否译文: 发表时间:2017-03-01 合写作者:傅仁利,徐月芳 通讯作者:王旭东