摘要:This article discusses about the significance of graphene oxide (GO) deposition on the surface of a titanium plate by electrophoretic deposition (EPD) method to improve the adhesive strength of Ti/polyetheretherketone (PEEK) interfacial adhesive. Firstly, the anodic EPD method was applied to a water dispersion solution of GO, and then the morphology and the properties of titanium plate surface were characterized by scanning electron microscopy and contact angle measurements before and after GO deposition. Furthermore, the changes in the properties of GO after heating at 390 degrees C were characterized by Raman and Fourier transform infrared spectroscopies. According to the results of single lap tensile shear test, the adhesion strength of Ti/PEEK interface after the anodization and deposition of GO was 34.94 MPa, an increase of 29.2% compared with 27.04 MPa of sample with only anodization. Also, the adhesion strengths were 58.1 and 76.5% higher compared with the samples of only GO deposited (22.1 MPa) and pure titanium (19.8 MPa), respectively. (C) 2018 Society of Plastics Engineers
ISSN号:0272-8397
是否译文:否
发表时间:2019-03-01
合写作者:Lv, Yunfei,Nipon, Roy,Wang, Yifan,Duan, Lixiang,Hu, Jingling,Ding, Wenye,Ma, Wenliang,陶杰,Shi, Yu
通讯作者:潘蕾