Thermal Decomposition Synthesis of Graphene Nanosheets Anchored on Mn3O4Nanoparticles as Anodes in Lithium Ion Batteries
点击次数：
所属单位：
电子信息工程学院
发表刊物：
IOP Conf. Ser. Mater. Sci. Eng.
摘要：
Graphene nanosheets (GNS) anchored on Mn3O4nanoparticles have been successfully synthesized through in situ thermal decomposition of Mn (NO3)2without the use of any templates or surfactants. Mn3O4particles were coordinately distributed on the GNS surface. This was achieved by forming 3D nanostructures to avoid detrimental graphene layer stacking, and was characterized using a scanning electron microscope. The Mn3O4/GNS nanocomposite delivers an initial capacity of 1450 mAh g-1at a current density of 100 mA g-1. It also maintains a high reversible capacity of 930 mAh g-1even after 60 charge-discharge cycles without showing any apparent decay. © Published under licence by IOP Publishing Ltd.
ISSN号：
1757-8981
是否译文：
否
发表时间：
2018-02-15
合写作者：
Tang, Xihao,邱旦峰,卜刚,夏永君,Zhao, Bin,Lin, Zixia,Shi, Yi
通讯作者：
马晓平
发表时间：
2018-02-15
学位：管理学博士学位
职称：副教授
所在单位：经济与管理学院