Journal:J Mater Eng Perform
Abstract:The effect of 0.1 wt.% Co on the hot deformation behavior of fine-grained low-carbon microalloyed steel was investigated at temperatures of 850-1200 °C and a strain rate of 5 s−1. Furthermore, the toughness of the steel with and without Co at sub-zero temperatures was evaluated. The results suggest that the addition of 0.1 wt.% Co increases the flow stress and delays the occurrence of dynamic recrystallization (DRX) at the same deformation temperature and strain. The DRX fraction of steel specimens without and with 0.1 wt.% Co was about 67.4 and 43.9% at 850 °C, respectively. Then, it increased to 100% at 1100 °C. Compared with steel without Co, cementite particles in the tempered sorbite of steel with 0.1 wt.% Co decreased in size but increased in quantity, yield strength increased from 756 to 787 MPa, and Charpy V-notch energy at − 20 and − 50 °C improved from 69 and 41 to 102 and 65 J, respectively. The fracture morphology and crack propagation characteristics were consistent with the variation in impact energy. © 2017, ASM International.
ISSN No.:1059-9495
Translation or Not:no
Date of Publication:2018-01-01
Co-author:周双双,Liu Zili,侯志国,田青超
Correspondence Author:lxq