Exploiting Magnetism and Magnetocaloric Effect in Nd0.55Sr0.45Mn0.98Ga0.02O3
点击次数:
所属单位:理学院
发表刊物:JOURNAL OF SUPERCONDUCTIVITY AND NOVEL MAGNETISM
关键字:Manganite Magnetocaloric effect Phase transitions
摘要:We report results of the magnetization and magnetocaloric effect in lightly Ga-doped perovskite manganites Nd0.55Sr0.45Mn0.98Ga0.02O3. It undergoes a second-order paramagnetic to ferromagnetic transition at T-C = 250 K and shows a strong ferromagnetic properties below TC. However, an obvious upward deviation from the Curie-Weiss law far above TC indicates the existence of non-Griffiths-like behavior in paramagnetic phase. Together with the measurements of isothermal magnetization around the Curie temperature, the unsaturated magnetization curves under high magnetic field of 7.0 T imply that the Ga-substitution causes the formation of antiferromagnetic phase due to some localized charge order phases generated in this composition. Based on the data of isothermal magnetization measured around TC and Maxwell relation, we have calculated the maximum isothermal magnetic entropy change of 6.23 J/kg K for Delta mu H-0= 7.0 T magnetic field variation. Though only a moderate magnetic entropy change were obtained, a considerable large relative cooling power of 260 J/kg for Delta mu H-0= 7.0 T and 182 J/kg for Delta mu H-0 = 5.0 T were found in this sample, this ensure it to be a potential candidate material to be applied in the magnetic refrigeration.
ISSN号:1557-1939
是否译文:否
发表时间:2017-08-01
合写作者:Yu, Bo,Han, Hui,张卫纯,Zhang, Lei,樊济宇
通讯作者:兰秀风,樊济宇