关键字：Oxidation behavior Magnetron sputtering High temperature Al-Y coating gamma-TiAl alloy Diffusion

摘要：In this study, an Al-Y coating was applied to enhance the property of oxidation resistance on the surface of gamma-TiAl alloys by rf magnetron sputtering. The isothermal oxidation tests were investigated at 900 degrees C for 100 h. The coating characteristics and microstructure of coating after isothermal oxidation were inspected by XRD and SEM methods respectively, and coating bonding strength was investigated by scratch tester. Results show that Al2O3 and Y2O3 were produced on the surface of gamma-TiAl alloys to enhance oxidation resistance during the isothermal oxidation test. Diffusion layer with rich element of Al provides abundant Al to surface for formation of a continuous Al2O3 layer which increases oxidation resistance effectively. Oxides of YA1O(3) and YAG were formed during the oxidation tests, which were beneficial for the strength, hardness and fracture toughness of crystal grain of Al2O3. Furthermore, Element of Ti diffused into surface from substrate was restrained by Al because of the formation of TiAl3 and TiAl, which avoid the layer-broken by titanium oxides with porous structure

ISSN号：1517-7076

是否译文：否

发表时间：2019-01-01

合写作者：Yang, Z. G.,Miao, Q.,Hu, R. Y.,Song, Y. P.

通讯作者：梁文萍