Damage development and lifetime prediction of cross-ply ceramic-matrix composites subjected to cyclic loading at room and elevated temperatures
点击次数：
所属单位：民航学院
发表刊物：ADVANCES IN APPLIED CERAMICS
关键字：Ceramic-matrix composites airworthiness damage evolution oxidation matrix multicracking interface debonding
摘要：In this paper, the damage development and lifetime prediction of fibre-reinforced ceramic-matrix composites subjected to cyclic loading at elevated temperatures in oxidising atmosphere have been investigated. Considering the damage mechanisms of matrix cracking, interface debonding, interface wear and interface oxidation, the damage evolution of fatigue hysteresis dissipated energy, fatigue hysteresis modulus, fatigue peak strain, interface shear stress and broken fibres fraction have been analysed. The relationships between damage parameters and internal damage of matrix cracking, interface debonding and slipping, and fibres fracture have been established. The experimental fatigue hysteresis, interface slip lengths, peak strain, and the fatigue life curves of cross-ply CMCs under cyclic loading at elevated temperature have been predicted. The different fatigue behaviour in unidirectional and cross-ply CMCs at room and elevated temperatures subjected to low-cycle and high-cycle fatigue has been discussed.
ISSN号：1743-6753
是否译文：否
发表时间：2018-01-01
通讯作者：李龙彪
上一条：Synergistic Effects of Temperature, Oxidation and Stress Level on Fatigue Damage Evolution and Lifetime Prediction of Cross-Ply SiC/CAS Ceramic-Matrix Composites Through Hysteresis-Based Parameters
下一条：In-phase thermomechanical fatigue damage evolution of long fiber-reinforced ceramic-matrix composites using fatigue hysteresis-based damage parameters