Damage development and lifetime prediction of fiber-reinforced ceramic-matrix composites subjected to dwell-fatigue loading at elevated temperatures in oxidizing atmosphere
点击次数：
所属单位：民航学院
发表刊物：JOURNAL OF THE CERAMIC SOCIETY OF JAPAN
关键字：Ceramic-matrix composites (CMCs) Dwell-fatigue Damage evolution Oxidation Matrix multicracking Interface debonding
摘要：In this paper, the damage development and lifetime prediction of fiber-reinforced ceramic-matrix composites subjected to the dwell-fatigue loading at elevated temperatures in oxidizing atmosphere have been investigated using the micromechanics approach. Considering the damage mechanisms of matrix multicracking, fiber/matrix interface debonding, interface wear and interface oxidation and fibers fracture, the damage evolution of the fatigue hysteresis dissipated energy, fatigue hysteresis modulus, fatigue peak strain and broken fibers fraction have been analyzed. The relationships between the fatigue hysteresis-based damage parameters and the internal damage development of matrix multicracking, fiber/matrix interface debonding and sliding and fibers fracture have been established. The experimental dwell-fatigue damage development and fatigue lifetime curves of crossply Nicalon (TM)-SiC/MAS and 2D Sylramic (TM)-SiC/SiC composites subjected to the dwell-fatigue loading at elevated temperatures in air and in steam conditions have been predicted. (C) 2018 The Ceramic Society of Japan. All rights reserved.
ISSN号：1882-0743
是否译文：否
发表时间：2018-07-01
通讯作者：李龙彪