Effects of Temperature and Oxidation on Cyclic-Fatigue Life of 2D Woven Ceramic-Matrix Composites
点击次数：
所属单位：民航学院
发表刊物：JOURNAL OF AEROSPACE ENGINEERING
关键字：Ceramic-matrix composites (CMCs) Fatigue S-N curve Oxidation
摘要：In this paper, the effects of temperature and oxidation on cyclic-fatigue life of two dimensional (2D) woven SiC/SiC ceramic-matrix composites (CMCs) have been investigated. The relationships between fatigue life, fibers failure, interface shear stress and fibers strength degradation, temperature, and oxidation have been established using micromechanical approach. The tension-tension fatigue life S-N curves of 2D SiC/SiC composite at room and elevated temperatures in moisture, argon, air, and steam have been predicted. It was found that the presence of steam causes accelerated damage evolution and degradation in fatigue life compared with that in air. (C) 2017 American Society of Civil Engineers.
ISSN号：0893-1321
是否译文：否
发表时间：2017-07-01
通讯作者：李龙彪