Modeling strength degradation of fiber-reinforced ceramic-matrix composites under cyclic loading at room and elevated temperatures
点击次数：
所属单位：民航学院
发表刊物：MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
关键字：Ceramic-matrix composites (CMCs) Airworthiness Strength Matrix cracking Interface debonding Fibers failure
摘要：In this paper, the strength degradation of fiber-reinforced ceramic-matrix composites (CMCs) under cyclic loading at room and elevated temperatures has been investigated. The shear-lag model combined with the matrix statistical multiple cracking model, interface debonding criterion and fiber fracture model has been adopted to analyze the stress distributions in damaged CMCs, considering the damage mechanism of the interface wear. The relationships between the residual strength and peak stress, interface debonding, fiber failure and cycle number have been established. The effects of fatigue peak stress, initial and steady-state interface shear stress, fiber Weibull modulus and fiber strength on the degradation of residual strength and fibers failure have been investigated. The evolution of residual strength versus cycle number curves of fiber-reinforced CMCs under cyclic loading at room and elevated temperatures have been predicted.
ISSN号：0921-5093
是否译文：否
发表时间：2017-05-17
通讯作者：李龙彪