Remarkable microwave absorption performance of ultralight graphene- polyethylene glycol composite aerogels with a very low loading ratio of graphene
点击次数:
发表刊物:Composites Part A
摘要:Graphene/polyethylene glycol (GPEG) composite aerogels were fabricated by the reduction-assembly of gra-
phene oxide (GO) in polyethylene glycol 400 (PEG400) and the following freeze-drying process. PEG400 can
effectively avoid the agglomeration of graphene sheets and adjust the permittivity of GPEGs. These GPEGs show
an outstanding improvement on microwave absorption performance when the additive amount of GO is 5–25wt
%. The minimum reflection loss (RL) can reach −43.2 dB at 13.8 GHz, and the effective absorption bandwidth
(RL < −10 dB) was 5.30 GHz (9.6–14.9 GHz) with the absorber thickness of 2.35 mm when the additive
amount of GO in absorber is only 7.5wt%. These composite aerogels still maintain an ultralight nature (the
density of 18.5–19.8 mg/cm 3 ). This work provides a facile preparation method to fabricate an exceptional mi-
crowave absorption material which possesses lightweight, economy and the high-efficient microwave absorption
property.
论文类型:期刊论文
文献类型:J
卷号:123
页面范围:158-169
是否译文:否
发表时间:2019-05-01
收录刊物:SCIE
附件:
上一条:Ultralight graphene aerogel enhanced with transformed micro-structure led by polypyrrole nano-rods and its improved microwave absorption properties
下一条:Constructing excellent electromagnetic wave absorber with dielectric- dielectric media based on 3D reduced graphene and Ag(I)-Schiff base coordination compounds