所属单位：材料科学与技术学院
发表刊物：Diamond Relat. Mat.
摘要：In this work, diamond/Cu-1Cr composite coatings were successfully prepared on T2 Cu substrate via mechanical milling method. The effects of high temperature annealing on the microstructure, wear resistance and thermal conductivity of coatings have been studied. The results showed that the diffusion ability of copper and chromium was enhanced to form segregation after annealing at 700 °C, while chromium carbides were formed on the surface of diamond. When the annealing temperature was higher than 800 °C, the loose lamellar structure was formed from the surface to the inside of the coating. The friction coefficient of the annealed coating at light load was lower than that of the unannealed coating, much lower than that of pure copper. The wear resistance of the unannealed coating was far superior to that of pure copper, but it decreased slightly after annealing. After annealing at 700 °C, the thermal conductivity of the coated sample was significantly improved to 346.91 W·m−1·K−1. Increasing the annealing temperature would result in the deterioration of heat conduction. © 2019
ISSN号：0925-9635
是否译文：否
发表时间：2019-08-01
合写作者：Lu, Congyang,沈以赴,Tian, Ye,张天野,Jiang, Jian,蒋建林,Hu, Linquan
通讯作者：Lu, Congyang,冯晓梅
发表时间：2019-08-01