Synthesis and luminescence enhancement of CaySr4?x?yAl2O7:xEu2+phosphors by a novel halide-assisted solid-state reaction method
点击次数：
所属单位：
材料科学与技术学院
发表刊物：
J Mater Sci Mater Electron
摘要：
Eu2+doped strontium aluminate phosphors CaySr4−x−yAl2O7:xEu2+(0 ≤ x ≤ 0.1, 0 ≤ y ≤ 0.1) were synthesized via a novel halide-assisted solid-state reaction method. The phase structure and photoluminescence properties of CaySr4−x−yAl2O7:xEu2+were characterized via X-ray diffraction (XRD) and fluorescence spectrophotometer. The XRD patterns indicate that the α-Sr4Al2O7phase structure with negligible impurities were produced in the samples of CaySr4−x−yAl2O7:xEu2+(x ≤ 0.1 and y ≤ 0.1) at 1450 °C. Photoluminescence results show that the CaySr4−x−yAl2O7:xEu phosphor with NH4I as reductant presents typical intense Eu2+red emission bands centered at 610 nm while excited by 450 nm. Accordingly, samples without NH4I only exhibit two weak Eu3+emission peaks located at 598 and 619 nm, respectively. It can be ascribed to the reduction characteristic of I−ion. Furthermore, by partial replacement of Sr2+with Ca2+in Sr4Al2O7host, the emission intensity is enhanced up to 260% with emission peak red shifted by 5–10 nm. These results indicate that partial substitution of Sr2+by Ca2+is an efficient way to increase the proportion of longer wavelength emission and luminescence intensity for Sr4Al2O7:Eu phosphors. © 2018, Springer Science+Business Media, LLC, part of Springer Nature.
卷号：
29
期号：
12
页面范围：
10487-10493
ISSN号：
0957-4522
是否译文：
否
发表时间：
2018-06-01
收录刊物：
EI
发表时间：
2018-06-01
学位：工学博士学位
职称：教授
所在单位：材料科学与技术学院