发表刊物:JOURNAL OF POROUS MATERIALS
关键字:Carbon foam SiO2 aerogel Composite Thermal conductivity
摘要:In this study, carbon foam (CF) and SiO2 aerogel composite were prepared by the sol-gel method under a circumstance of the atmospheric drying process. The Pyrolysis mechanism of carbon foam was investigated through thermal gravimetric analysis and Fourier transform infrared spectroscopy (FTIR). Carbon foam having ultralight properties with a density of 5.44 kg/m(3), functions as a skeleton to support the composite. The maximum compressive stress measured for CF/SiO2 aerogel composite was about 1.0 MPa. At room temperature, the measured thermal conductivities of the CF and CF/SiO2 aerogel composite were 0.035 W/m K and 0.024 W/m K, while at 300 degrees C, it was reported to be 0.120 W/m K and 0.057 W/m K. Aerogel filled in carbon foam cells have significantly reduced the gaseous thermal conductivity of the prepared composite.
ISSN号:1380-2224
是否译文:否
发表时间:2019-10-01
合写作者:Liu, Yang,Zhang, Junxiong,Ai, Sufen,Tang, Hao,唐豪
通讯作者:陈照峰