Fire retardant mechanism of PA66 modified by a "trinity" reactive flame retardant

Hits:

Affiliation of Author(s):材料科学与技术学院

Title of Paper:Fire retardant mechanism of PA66 modified by a "trinity" reactive flame retardant

Journal:JOURNAL OF APPLIED POLYMER SCIENCE

Key Words:flame retardance microscopy polycondensation resins spectroscopy

Abstract:A "trinity" reactive flame retardant (TRFR) was successfully synthesized from pentaerythritol, phosphorus oxychloride (POC), and p-aminobenzoic acid in two steps. The flame retardant polyamide 66 (PA66) was prepared by polymerizing TRFR with PA66 salt; the structural changes during the heating process, the morphology, and composition after combustion of flame retardant PA66 were analyzed. Fourier transform infrared, scanning electron microscopy, and Raman analysis results showed that the TRFR structure on flame retardant PA66 decomposed at the temperature of 25-550 degrees C, forming compounds containing phosphorus, carbon, and nitrogen, respectively. These compounds promoted the dehydration of the combustion surface to form char, increased the char formation rate, and produced nonflammable gases, resulting in a dense, porous, noncombustible carbon layer. The carbon layer may isolate oxygen and heat, thereby preventing the polymer from sustainability of combustion. When the TRFR salt content was 3%, TRFR flame retardant PA66 has excellent flame retardancy with limited oxygen index value of 29 and UL94 of V-0 rating. (c) 2019 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2020, 137, 47488.

ISSN No.:0021-8995

Translation or Not:no

Date of Publication:2020-01-05

Co-author:Fu, Hao,Lv, Jipeng

Correspondence Author:cyh

Pre One:PEEK导热性能研究进展

Next One:The process and mechanism research of in situ deposited NANO-SIO2 on the surface of jute fiber