Effects of aging process in hot forming with synchronous cooling on properties of AA2024
发表时间:2020-11-30 点击次数:
所属单位:机电学院
发表刊物:Key Eng Mat
摘要:Aging treatment is an important process of a new hot forming technology with synchronous cooling(HFSC) for heat-treatable, high-strength aluminum alloys. In this paper, it were carried out respectively experimental research both the artificial aging and natural aging, and subsequent performance testing and microstructure analysis were implemented to investigation the effect of different aging process on the final mechanical properties of AA2024. Research results show that, under the condition of forming temperature range from 475°C to 495°C, the mechanical properties of AA2024 which made by HFSC and after nature aging for 96 hours: yield strength, tensile strength and elongation ratio was up to 499.0MPa, 306.5 MPa and 19.1% respectively; For the artificial aging, at aging temperature of 190°C, aging time of 4∼8 hour, its yield strength, tensile strength and elongation ratio was up to 515.0MPa, 398.0 MPa and 11.1% respectively. © 2017 Trans Tech Publications, Switzerland.
ISSN号:1013-9826
是否译文:否
发表时间:2017-01-01
合写作者:李成玲,王娜
通讯作者:陈明和
发表时间:2017-01-01